CFB5500 – BIAXIALY ORIENTED NYLON/POLYETHYLENE

    is a dual layer high clarity film designed to provide protection for those products having a high degree of sensitivity to moisture.  Having an extended shelf life, a very low Moisture Vapor Transmission Rate (M.V.T.R.) as well as an equally low Oxygen Transmission Rate (O.T.R.), CFB5500 will meet all of your critical packaging needs.  5 Mil Biax is a very strong and clear material designed for tough applications.  It is typically specified for large bags that must carry a heavy load.  The film does not stretch due to the orientation of the layers during the laminating process. 
    Material:
    Biaxially Oriented Nylon / Polyethylene
    Available As:
    2-seal pouch, 3-seal pouch, stand up pouch, sheets & tubing
    Clarity:
    Transparent
    Thickness:
    5 Mil

    COMPOS-A-CLEAN™ Specs

    Film Properties
    ASTM Method
    Typical Value
    Units
    Tensile Strength
    MD
    ASTM D-882
    34
    lbs. at break
    XMD
    ASTM D-882
    36
    lbs. at break
    Tear
    MD
    ASTM D-882
    64
    lbs. at break
    XMD
    ASTM D-882
    64
    lbs. at break
    M.V.T.R.
    ASTM F-1249
    0.184
    gm/100sq.in./24 hrs
    O.T.R.
    Mocon
    2.0
    cc/100sq.in./24 hrs
    Burst
    Mullen
    85
    PSI

    Note: The values indicated in this document are the results of tests made in compliance with the normal standards.  They are given as an indication and should be considered as average values and given without any obligation on our part.

    Compos-A-Clean Data Sheet