COMPOS-A-CLEAN™

CFB5500 - BIAXIALY ORIENTED NYLON/POLYETHYLENE
is a dual layer high clarity film designed to provide protection for those products having a high degree of sensitivity to moisture.  Having an extended shelf life, a very low Moisture Vapor Transmission Rate (M.V.T.R.) as well as an equally low Oxygen Transmission Rate (O.T.R.), CFB5500 will meet all of your critical packaging needs.  5 Mil Biax is a very strong and clear material designed for tough applications.  It is typically specified for large bags that must carry a heavy load.  The film does not stretch due to the orientation of the layers during the laminating process.
 

Physical Properties
Material	Biaxialy Oriented Nylon / Polyethylene
Available As:	Bags & Sheets
Clarity:	Transparent
Thickness:	5 Mil

 

Film Properties	ASTM Method	Typical Value	Units
Tensile Strength
MD	ASTM D-882	34	lbs. at break
XMD	ASTM D-882	36	lbs. at break
Tear
MD	ASTM D-882	64	lbs. at break
XMD	ASTM D-882	64	lbs. at break
M.V.T.R.	ASTM F-1249	0.184	gm/100sq.in./ 24 hrs
O.T.R.	Mocon	2.0	cc/100sq.in./ 24 hrs
Burst	Mullen	85	PSI

 

Note: The values indicated in this document are the results of tests made in compliance with the normal standards.  They are given as an indication and should be considered as average values and given without any obligation on our part.

Please also see our full list of available Cleanroom Packaging Materials.